Imperalum, was founded as a company in 1968, and is currently one of the most important manufacturers in the Iberian Peninsula of waterproofing bituminous products, and is also the leader in Portugal in the sale of thermal and acoustic insulation...
Polyster R 50 V
Bitumen sheets for waterproofing
POLYSTER® R50 V is a waterproofing bituminous sheet: 5,0 Kg/m2 APP polymer concrete membrane, double-reinforced with 50 gr/m2 fibreglass reinforcement and 250 gr/m2 polyester reinforcement, protected with polyethylene on the bottom surface and with sand on the top surface.
Used in accessible coatings movement permanence of vehicles and bridge platforms and viaducts.
POLYSTER® R50 V is a waterproofing bituminous sheet: 5,0 Kg/m2 APP polymer concrete membrane, double-reinforced with 50 gr/m2 fibreglass reinforcement and 250 gr/m2 polyester reinforcement, protected with polyethylene on the bottom surface and with sand on the top surface.
Used in accessible coatings movement permanence of vehicles and bridge platforms and viaducts.
| System |
Category |
Code |
|
Masterformat 14
|
Dampproofing and Waterproofing
|
07 10 00
|
|
Omniclass
|
Waterproofing
|
23-13 25 17
|
|
Uniclass 2.0
|
Waterproofing Concrete Admixtures
|
Pr_20_31_14_96
|
|
Uniclass 2015
|
Waterproofing concrete admixtures
|
Pr_20_31_03_95
|
|
Asset Type
|
Fixed
|
|
Bituminous mixture
|
Modified bitumen APP AVANCE
|
|
Colour
|
Black
|
|
Colour Description
|
N/A
|
|
Constituents
|
N/A
|
|
Eco recommendations
|
The selective separation and the forwarding of the waste from the application of these products are of the sole responsibility of the applier or user and should be done in accordance with applicable legislation. The residues of Imperalum bituminous membranes were analyzed in accredited laboratory and classified as nonhazardous according to the Decree-Law n º 183/2009, which establishes the legal regime of the deposition of waste landfilled in Portugal.
|
|
Features
|
N/A
|
|
Finish / Cladding
|
Bottom layer – Thermofusible polyethylene film, Top layer – Mineral granules
|
|
Frame
|
Polyester carrier, Fibreglass carrier
|
|
Material
|
N/A
|
|
Material Description
|
Bituminous mixture enhanced for high temperatures, with performance levels between -5°C and +130°C.
|
|
Nominal Height
|
N/A
|
|
Nominal Length
|
N/A
|
|
Nominal Thickness
|
3.8
|
|
Nominal Width
|
N/A
|
|
Nominal mass per unit area
|
5.0 ± 0.3
|
|
Piece
|
8.0 m2 rolls (1.0 m x 8.0 m), with a nominal weight of 40.0 Kg and straightness ≤ 20 mm/10 m
|
|
Pieces per pallet
|
25
|
|
Size (WxLxH or D)
|
N/A
|
|
Storage Conditions / Shelf-Life
|
Avoid falls and knocks. Transport and store rolls vertically, always protected from the weather – i.e. sun, rain, frost, hail, snow. Raise rolls, always in their pallets, using a crane or stacker. For more specific information on transportation, handling and other characteristics, please see the Safety Specifications.
|
|
Type
|
N/A
|
|
Weight
|
40 g
|
|
Manufacturer
|
Imperalum
|
|
Model
|
Polyster R 50 V
|
|
Reference
|
POLYSTERR50V
|
|
Product Version
|
V1
|
|
Publication Date
|
27-03-2018
|
|
CE Marking
|
Yes
|
|
Product Website
|
|
|
Range
|
Betume App Advance
|
|
Sold In
|
N/A
|
|
Embodied Carbon (kg CO2 eq/m2)
|
N/A
|
|
Green Certifications
|
N/A
|
|
Manufactured in (City)
|
Montijo
|
|
Manufactured in (Country)
|
Portugal
|
|
Recyclable Materials
|
N/A
|
|
Recycled Content
|
N/A
|
|
Application
|
Exterior
|
|
Behaviour during application of mastic asphalt
|
0 %
|
|
Behaviour during application of mastic asphalt.
|
≤ 1 mm
|
|
Bond strength (concrete) (N/mm2)
|
≥ 0.6
|
|
Building Types
|
Bridges & Viaducts
|
|
Certifications
|
N/A
|
|
Code Performance
|
N/A
|
|
Compatibility by heat conditioning (91 days, 50 ºC
|
≤ 150 %
|
|
Crack bridging ability (10.000 cycles)
|
0 °C
|
|
Dimensional stability
|
≤ 0.5 %
|
|
Durability Flexibility
|
5 ± 5 °C
|
|
Durability behaviour at high temperatures
|
120 ± 10 °C
|
|
External fire performance (X roof (t1))
|
B roof (t1)
|
|
Flexibility at low temperature
|
-5 °C
|
|
Flow resistance at elevated temperature
|
120 °C
|
|
Granular adhesion
|
N/A
|
|
Longitudinal Tensile strength (N/5cm)
|
1100 ± 220
|
|
Longitudinal elongation at break
|
35 ± 15 %
|
|
Longitudinal resistance to tearing (nail shank)
|
≥ 150 N
|
|
Reaction to fire (Class)
|
E
|
|
Resistance to compaction of an asphalt layer
|
Yes
|
|
Resistance to impact
|
≥ 1000 mm
|
|
Resistance to root penetration
|
N/A
|
|
Resistance to static loading
|
≥ 15 kg
|
|
Shear resistance of joints (N/5cm)
|
600 ± 100
|
|
Shear strength (N/mm2)
|
≥ 0.3
|
|
Transversal elongation at break
|
35 ± 15 %
|
|
Transversal resistance to tearing (nail shank)
|
≥ 150 N
|
|
Transversal tensile strength (N/5cm)
|
850 ± 170
|
|
Use
|
N/A
|
|
Water Tightness
|
Yes
|
|
Water absorption
|
≤ 8
|